首页> 外文期刊>Journal of structural chemistry >Phase formation in mixed TiO_2-ZrO_2 oxides prepared by sol-gel method
【24h】

Phase formation in mixed TiO_2-ZrO_2 oxides prepared by sol-gel method

机译：溶胶-凝胶法制备TiO_2-ZrO_2混合氧化物的相形成

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Pure titania, zirconia, and mixed oxides (3-37 mol.% of ZrO_2) are prepared using the sol-gel method and calcined at different temperatures. The calcined samples are characterized by Raman spectroscopy, X-ray powder diffraction, scanning electron microscopy, transmission electron microscopy, and nitrogen adsorption porosimetry. Measurements reveal a thermal stability of the titania anatase phase that slightly increases in the presence of 3-13 mol.% of zirconia. Practically, the titania anatase-rutile phase transformation is hindered during the temperature increase above 700°C. The mixed oxide with 37 mol.% of ZrO_2 treated at 550°C shows a new single amorphous phase with a surface area of the nanoparticles double with respect to the other crystalline samples and the formed srilankite structure (at 700°C). The anatase phase is not observed in the sample containing 37 mol.% of ZrO_2. The treatment at 700°C causes the formation of the srilankite (Ti _(.63)Zr_(0.37)O_x) phase.
机译：使用溶胶-凝胶法制备纯的二氧化钛，氧化锆和混合氧化物（3-37摩尔％的ZrO_2），并在不同温度下煅烧。煅烧样品通过拉曼光谱，X射线粉末衍射，扫描电子显微镜，透射电子显微镜和氮吸附孔隙率法进行表征。测量表明，在3-13mol。％的氧化锆存在下，二氧化钛锐钛矿相的热稳定性略有增加。实际上，在高于700℃的温度升高期间，二氧化钛锐钛矿-金红石相转变受到阻碍。在550℃下处理的具有37mol％的ZrO 2的混合氧化物显示出新的单一非晶相，该纳米颗粒的表面积相对于其他晶体样品为两倍，并且形成了绢晶结构（在700℃）。在含有37mol。％的ZrO_2的样品中未观察到锐钛矿相。在700°C下进行处理会导致生成绢云母（Ti _（。63）Zr_（0.37）O_x）相。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号