首页> 外文期刊>Polymer Composites >The carbon nanotubes effects on the morphology and properties of poly(lactic) acid/poly(butylene adipate‐co‐terephthalate) blends
【24h】

The carbon nanotubes effects on the morphology and properties of poly(lactic) acid/poly(butylene adipate‐co‐terephthalate) blends

机译：The carbon nanotubes effects on the morphology and properties of poly(lactic) acid/poly(butylene adipate‐co‐terephthalate) blends

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相关主题

摘要

Abstract Poly(lactic acid) (PLA), as a biodegradable semicrystalline thermoplastic, is usually blended with degradable poly(butylene‐adipate‐co‐terephthalate) (PBAT) to improve toughness for the sake of environmental concerns. To obtain controllable properties of PLA/PBAT composites, the use of nanoparticles is increasing from a technical point of view, thus making the blends more widely used in the final products. In this study, immiscible blends of PLA and PBAT (70/30 wt) and PLA/PBAT with different carbon nanotube (CNT) contents (0.5, 1, and 2 wt) were prepared using a twin‐screw extruder followed by injection molding. The preferential distribution of CNTs in the PBAT phase was characterized by SEM and thermodynamic analysis, and reason for selective localization is discussed. The morphology of the PLA/PBAT composite showed PBAT particles dispersed within the PLA matrix with an average diameter of 0.38 μm. For the nanocomposites, the CNTs in the minor PBAT phase produced larger elongated PBAT domains with a maximum average diameter of 1.3 μm. The elongation at break of binary PLA/PBAT blends was 160.9, while the maximum elongation at break of the nanocomposite was 294.3. Additionally, the influence of CNTs on the crystallization behavior and rheological and mechanical properties of PLA/PBAT/CNT blends was systematically investigated.

著录项

获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号