首页> 外文期刊>Polymer Composites >3D printing of a composite iPP/quill of chicken feathers functionalized with pimelic acid
【24h】

3D printing of a composite iPP/quill of chicken feathers functionalized with pimelic acid

机译：3D printing of a composite iPP/quill of chicken feathers functionalized with pimelic acid

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相关主题

摘要

Abstract In this work, the thermomechanical properties of an isotactic polypropylene (iPP)/quill composite were evaluated. This reinforcement was added at 0.5, 1.0 and 5.0 wt% in the iPP matrix. The reinforcement was previously subjected to alkaline treatment with NaOH (QT) and chemical functionalization with pimelic acid (PA) to produce an effective β‐crystal nucleating agent. This functionalization was characterized by Fourier transform infrared spectroscopy (FTIR), showing the presence of a new band at 1571 cm−1 associated with the carboxylate group of pimelic acid, indicating a bond between PA and the quill surface. The internal geometry of the specimens obtained by 3D printing were studied by scanning electron spectroscopy (SEM). The effectiveness of the modified reinforcement as a promoter of the β‐crystalline phase was evaluated by differential scanning calorimetry (DSC) and wide angle X‐ray scattering (WAXD) under non‐isothermal crystallization conditions due to the 3D printing process. The composite that showed a higher Kβ index was 1.0% with a value of 64% by DSC and 65% by WAXD. Furthermore, the thermomechanical properties were characterized by dynamic mechanical analysis (DMA) where, for the 0.5% and 1.0% composites, the storage modulus (E') was higher compared to neat iPP. However, for the 5.0% composite the E' values were lower.

著录项

获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号