硫改性镍催化剂丁烯-1双键临氢异构性能

         

摘要

将Ni/Al2O3催化剂浸渍于有机多硫化物(TPS-37)中制备得到硫改性Ni/Al2O3催化剂.采用X射线荧光光谱(XRF)、热重-质谱(TG-MS)联用、X射线光电子能谱仪(XPS)和程序升温还原(TPR)等方法对催化剂进行表征,并考察了硫改性Ni/Al2O3催化剂上丁烯-1双键临氢异构性能.结果表明,硫改性Ni/Al2O3催化剂经高温氢气活化及甲苯萃取后,催化剂上硫含量基本不变.硫与催化剂之间存在较强的相互作用,使氧化镍在相对较低的温度下被H2还原;硫改变了Ni金属周围电子环境,从而显著改善催化剂的双键临氢异构性能.在反应温度60℃,氢压1.6 MPa,氢气和碳四烃物质的量之比(氢烃比)为0.013的条件下,硫改性Ni/Al2O3催化剂催化丁烯-1双键临氢异构反应,丁烯-1转化率可达92.6%,丁烯-2选择性为97.5%.催化剂稳定性实验结果表明,硫改性催化剂催化性能好,稳定性优良.%The sulfur-modified Ni-based catalysts were prepared by the incipient wetness impregnation technique with the Ni/Al2O3 in solution of organic polysulfide. The catalysts were characterized by X-ray fluorescence (XRF), thermogravimetry-mass spectrometry (TG-MS), X-ray photoelectron spectroscopy (XPS) and temperature-programmed reduction (TPR).The performance of sulfur-modified Ni/Al2O3 catalyst on hydrogen isomerization of 1-butene double bond was investigated. The results showed that the sulfur content of the sulfur-modified Ni/Al2O3 catalyst was almost unchanged after the activation of high temperature hydrogen and extraction with toluene. Since there was a strong interaction between the sulfur and the catalyst, nickel oxide was reduced by hydrogen at relatively low temperature. Sulfur changed the electronic environment around the Ni metal, thereby significantly improved the hydroisomerization of the catalyst at the double bond. The conversion up to 92.6%, selectivity of 2-butene 97.5% were obtained when sulfur modified Ni/Al2O3 catalyst was used to catalyze the hydroisomerization of 1-butene under the operation conditions of temperature 60℃, hydrogen pressure 1.6 MPa and the molar ratio of H2 to C40.013. The catalyst stability tests demonstrated that the sulfur- modified Ni/Al2O3 performed excellent with good stability.

著录项

  • 来源
    《化学反应工程与工艺》 |2017年第4期|305-311|共7页
  • 作者单位

    华东理工大学 化学工程联合国家重点实验室,上海 200237;

    中国石油化工股份有限公司上海石油化工研究院绿色化工与工业催化国家重点实验室,上海 201208;

    中国石油化工股份有限公司上海石油化工研究院绿色化工与工业催化国家重点实验室,上海 201208;

    中国石油化工股份有限公司上海石油化工研究院绿色化工与工业催化国家重点实验室,上海 201208;

    华东理工大学 化学工程联合国家重点实验室,上海 200237;

    华东理工大学 化学工程联合国家重点实验室,上海 200237;

  • 原文格式 PDF
  • 正文语种 chi
  • 中图分类 催化反应;
  • 关键词

    硫; 镍; 丁烯-1; 临氢异构;

相似文献

  • 中文文献
  • 外文文献
  • 专利
获取原文

客服邮箱:kefu@zhangqiaokeyan.com

京公网安备:11010802029741号 ICP备案号:京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有
  • 客服微信

  • 服务号